No.10–60 · h 100–600 · St3sp5 / C245 / 09G2S · GOST 8239
I-beam GOST 8239
Hot-rolled I-beam with tapered inner flange faces, No. 10–60 to GOST 8239-89; nearest equivalents are IPN and GB/T 706
HW · HM · HN · h 100–600 · Q235B / Q355B · GB/T 11263
Wide-flange H-beam
Hot-rolled H-section with parallel flange faces to GB/T 11263: HW, HM, HN series, the counterparts of Sh, K, B to GOST R 57837
- GB/T 11263-2017
- GB/T 700-2006
- GB/T 1591-2018
- GOST R 57837-2017
- EN 10025-2:2019
- ASTM A992/A992M
- Q235B
- Q355B
- Q355C
Section
Key parameters
- Series
- HW, HM, HN
- Depth h
- 100–600 mm
- Flange width b
- 50–400 mm
- Web thickness s
- 5–13 mm
- Flange thickness t
- 7–21 mm
- Length
- 6–12 m, fixed length to specification
- Steel grade
- Q235B, Q355B; Q355C on project requirement
Sizes and weight
Common HW, HM and HN profiles to GB/T 11263
| Profile | h×b, mm | s, mm | t, mm |
|---|---|---|---|
| HW 100 | h×b, mm100×100 | s, mm6 | t, mm8 |
| HW 150 | h×b, mm150×150 | s, mm7 | t, mm10 |
| HW 200 | h×b, mm200×200 | s, mm8 | t, mm12 |
| HW 250 | h×b, mm250×250 | s, mm9 | t, mm14 |
| HW 300 | h×b, mm300×300 | s, mm10 | t, mm15 |
| HW 350 | h×b, mm350×350 | s, mm12 | t, mm19 |
| HW 400 | h×b, mm400×400 | s, mm13 | t, mm21 |
| HM 150 | h×b, mm150×100 | s, mm6 | t, mm9 |
| HM 200 | h×b, mm200×150 | s, mm6 | t, mm9 |
| HM 250 | h×b, mm250×175 | s, mm7 | t, mm11 |
| HM 300 | h×b, mm300×200 | s, mm8 | t, mm12 |
| HM 350 | h×b, mm350×250 | s, mm9 | t, mm14 |
| HM 400 | h×b, mm400×300 | s, mm10 | t, mm16 |
| HN 200 | h×b, mm200×100 | s, mm5.5 | t, mm8 |
| HN 250 | h×b, mm250×125 | s, mm6 | t, mm9 |
| HN 300 | h×b, mm300×150 | s, mm6.5 | t, mm9 |
| HN 350 | h×b, mm350×175 | s, mm7 | t, mm11 |
| HN 400 | h×b, mm400×200 | s, mm8 | t, mm13 |
| HN 450 | h×b, mm450×200 | s, mm9 | t, mm14 |
| HN 500 | h×b, mm500×200 | s, mm10 | t, mm16 |
| HN 600 | h×b, mm600×200 | s, mm11 | t, mm17 |
Sizes and masses follow the tables of the standard named in the table heading; rows that cannot be verified are not listed.
Theoretical weight at steel density 7.85 g/cm³. Actual batch weight is by scale and mill certificate.
Description
An I-section with parallel flange faces: the flanges are of uniform thickness across their full width, with no taper towards the web, so bolted connections need no tapered washers and welded splices are simpler. It is rolled on universal beam mills from continuously cast beam blanks. GB/T 11263 divides the profiles into series: HW, wide-flange, with depth close to flange width, used for columns; HM, medium-flange; HN, narrow-flange, working as beams. In GOST R 57837 the same roles are played by the Sh, K and B series, in EN by HEA, HEB and IPE.
Details
Steel grades are Q235B to GB/T 700 and Q355B to GB/T 1591; before 2018 the latter was designated Q345B. Q355B is low-alloy, with a yield strength of 355 MPa against 235 for Q235B, and carries more at the same section. Quality grade B denotes impact toughness at +20 °C; for cold climates the specification calls for grade C or D, tested at 0 °C and −20 °C. The size ranges of GB/T 11263 and GOST R 57837 do not match by number, so the specification is written in section dimensions h×b×s×t rather than by series designation alone.
During inspection at the mill we measure depth and flange width with callipers, web and flange thickness with a micrometer at three points along the length, check squareness of flanges to the web, camber and twist, and length; we examine the surface for laps and cracks. We compare the mill test certificate (MTC), its heat number, chemical composition (C, Si, Mn, P, S, and for Q355B also V, Nb, Ti) and mechanical properties, against the rolled-in mark on the beam and the bundle tag. Packing and loading are recorded with photographs in the inspection report.
Applications
- columns and girders of industrial building frames
- steel-framed hangars, warehouses and workshops
- floor and roof beams
- pipe racks and pipeline supports
- bridge and road structures
Packing and shipment
Profiles up to 300 mm deep are shipped in bundles strapped with steel band; larger ones as single pieces. Each beam carries the mill marking: steel grade, profile, heat number; the bundle carries a tag duplicating the certificate.
Grade equivalents
Equivalents are the nearest, not identical: the exact grade and standard are written into the contract.
| GOST | GB (China) | ASTM | EN | Note |
|---|---|---|---|---|
| St3sp5 / S245 | GB (China)Q235B | ASTMA36 | ENS235JR | NoteImpact toughness is specified at different temperatures: at −20 °C for St3sp5, at +20 °C for Q235B and S235JR. A cold-climate requirement is written into the specification separately. |
| S275 | GB (China)Q275B | ASTM— | ENS275JR | NoteNearest equivalent by yield strength; chemical composition and scope of testing differ between the three standards. |
| 09G2S / S345 | GB (China)Q355B | ASTMA572 Gr.50 | ENS355JR | NoteBefore GB/T 1591-2018 the grade was designated Q345B; certificates for earlier batches may still carry the old name. |
| S355 | GB (China)Q355C | ASTMA572 Gr.50 | ENS355J0 | NoteNearest equivalent by yield strength of 355 MPa; impact test temperature and method are specific to each of the three standards. |
| — | GB (China)Q355B | ASTMA992 Gr.50 | ENS355JR | NoteA992 is a grade for wide-flange beams with an upper limit on yield strength. Nearest equivalent, not an exact match. |
| — | GB (China)Q345P | ASTMA572 Gr.50 | ENS355GP | NoteSheet-pile grades. L4 and L5 to GOST 4781-85 are rolled from St3sp and St3ps; GOST has no dedicated sheet-pile grade. Nearest equivalent, not an exact match. |
Equivalents are the closest match, not identical: chemistry and tolerances differ between standards. The exact grade and standard are written into the contract.
The batch is checked against the order at the mill before shipment: sizes, markings, heat numbers on the certificate and tags, packing
Documents
What arrives with the steel
01
Mill test certificate (MTC)
Heat number, chemical composition, mechanical properties and standard for every heat in the batch.
02
Photo-documented inspection report
Measurements, markings, packing, weighing and bundle numbers, drawn up at the mill before shipment.
03
Specification and packing list
Items, sizes, quantities and mass by bundle: what the warehouse acceptance is checked against.
04
Certificate of origin
Confirms the mill and country of manufacture for customs clearance.
Related items
No.5–40 · U / P · h 50–400 · St3sp5 / 09G2S · GOST 8240
Channel GOST 8240
Hot-rolled channel No. 5–40 to GOST 8240-97: U series with tapered flange faces and P series with parallel faces
Buyer questions
How to read a mill test certificate (MTC) for structural sections
Four blocks are checked in the certificate. Standard and grade: the same as written in the specification, not an equivalent. Heat number: matches the marking on the profile and the bundle tag. Heat chemistry: C, Si, Mn, P, S, and for Q355B also V, Nb, Ti, within the grade limits. Mechanical properties: yield strength, tensile strength, elongation and impact toughness at the temperature the grade requires. The bureau checks the certificate against the batch at the mill before shipment and attaches it to the inspection report.
How Q235B differs from St3sp5 and S245
All three have a yield strength of 235 MPa, which is why design calculations treat them as equivalents. The differences lie in test conditions and deoxidation: St3sp5 is impact-tested at −20 °C, Q235B at +20 °C; the suffix sp denotes killed steel, while Q235B to GB/T 700 is supplied rimmed (F) or killed (Z). If the project calls for St3sp5, the specification sets the degree of deoxidation and the test temperature; the mill performs the tests and enters the results in the certificate.
How the tonnage of a section order is calculated
From the theoretical weight per metre in the standard's table: weight per metre × length × number of pieces. The actual weight of a batch differs from the theoretical weight within the standard's weight tolerance, so the contract fixes which weight the batch is settled on: theoretical or actual by weighing. GB and GOST profiles of the same number have different theoretical weights; the specification is calculated to the standard written in it.
What is checked when structural sections are inspected at the mill
Section geometry: depth and flange width with callipers, web and flange thickness with a micrometer, at several points along the length. Shape: squareness of flanges, camber and twist along the length, length. Surface: laps, scabs, cracks, pits. Documents: the mill test certificate against the heat number on the marking and the tag. Packing, piece count and loading, with photographs in the inspection report.
What the minimum batch is and whether different profiles can be combined in one delivery
The batch is sized to your volume; send us the specification. A mill rolls each size to its rolling schedule, so the bureau matches the specification items against mill schedules, assembles the delivery from one or several mills and inspects every batch before shipment.
Price request
Send your specification and we will quote your batch
Price depends on grade, size, tonnage and delivery terms on the day of contract.
Request received